Effect of Vacuum Carburizing on the Structure and the Properties of Aluminide Coatings on Nickel Superalloys
- Авторы: Abraimov N.1
-
Учреждения:
- Scientific–Production Center of Gas-Turbine Building SALYUT
- Выпуск: Том 2017, № 12 (2017)
- Страницы: 1052-1056
- Раздел: Hardening and Coating Technologies
- URL: https://journals.rcsi.science/0036-0295/article/view/171896
- DOI: https://doi.org/10.1134/S0036029517120023
- ID: 171896
Цитировать
Аннотация
The processes that occur during vacuum carburizing of turbine blades made of carbon-free nickel superalloys are considered. Disperse alloying-element carbide particles are found to form in the surface layer of the VZhM5 alloy. These particles increase the fatigue life of the alloy during high-temperature oxidation. The disperse carbide particles are shown to hinder the formation of coarse γ′-Ni3Al grains and topologically close-packed phases under a coating; hence, they prevent premature fracture of the alloy.
Ключевые слова
Об авторах
N. Abraimov
Scientific–Production Center of Gas-Turbine Building SALYUT
Автор, ответственный за переписку.
Email: diagnostika@salut.ru
Россия, Moscow