Interaction of niobium and tungsten monocarbides in molten copper
- Авторы: Bodrova L.1, Fedorova O.1, Shubin A.1, Pastukhov E.1
-
Учреждения:
- Institute of Metallurgy, Ural Branch
- Выпуск: Том 2017, № 3 (2017)
- Страницы: 204-208
- Раздел: Article
- URL: https://journals.rcsi.science/0036-0295/article/view/171345
- DOI: https://doi.org/10.1134/S003602951703003X
- ID: 171345
Цитировать
Аннотация
The chemical interaction of uncompacted monocarbide NbC and WC powders, which were taken at mass carbide ratios NbC: WC = 10: 1, 3: 1, 1: 1, and 1: 3 and a total carbide content of 20 wt %, in molten copper is studied at 1300°C. The primary and secondary phase transformations that result in the appearance and decomposition of an (Nb,W)C solid solution are analyzed. The activating role of low-frequency vibration is shown.
Об авторах
L. Bodrova
Institute of Metallurgy, Ural Branch
Автор, ответственный за переписку.
Email: berseneval@mail.ru
Россия, ul. Amundsena 101, Yekaterinburg, 620016
O. Fedorova
Institute of Metallurgy, Ural Branch
Email: berseneval@mail.ru
Россия, ul. Amundsena 101, Yekaterinburg, 620016
A. Shubin
Institute of Metallurgy, Ural Branch
Email: berseneval@mail.ru
Россия, ul. Amundsena 101, Yekaterinburg, 620016
E. Pastukhov
Institute of Metallurgy, Ural Branch
Email: berseneval@mail.ru
Россия, ul. Amundsena 101, Yekaterinburg, 620016
![](/img/style/loading.gif)