Influence of the precursor composition and the reduction conditions on the characteristics of magnesium-thermic niobium powders
- Авторы: Orlov V.1, Kryzhanov M.1
-
Учреждения:
- Tananaev Institute of Chemistry and Technology of Rare Elements and Mineral Raw Materials, Kola Science Center
- Выпуск: Том 2016, № 7 (2016)
- Страницы: 596-601
- Раздел: Article
- URL: https://journals.rcsi.science/0036-0295/article/view/170642
- DOI: https://doi.org/10.1134/S0036029516070107
- ID: 170642
Цитировать
Аннотация
The influence of the composition and the conditions of the reduction of niobium oxide compounds with magnesium vapor on the specific surface area of the produced metallic powder is studied. When magnesium niobate Mg4Nb2O9 is used as a precursor, the specific surface of the powder increases by several times compared to that of an Nb2O5 precursor. Niobium powders with the specific surface up to 150 m2 g–1 (calculated particle size 4.7 nm) and a bulk density of 0.8 g cm–3 are formed by the reduction of Mg4Nb2O9. The powders are characterized by a mesoporous structure, and the most part of the specific surface consists of pores with a diameter less than 4 nm.
Об авторах
V. Orlov
Tananaev Institute of Chemistry and Technology of Rare Elements and Mineral Raw Materials, Kola Science Center
Автор, ответственный за переписку.
Email: orlov@chemy.kolasc.net.ru
Россия, 26a, Academic town, Apatity, Murmansk oblast, 184209
M. Kryzhanov
Tananaev Institute of Chemistry and Technology of Rare Elements and Mineral Raw Materials, Kola Science Center
Email: orlov@chemy.kolasc.net.ru
Россия, 26a, Academic town, Apatity, Murmansk oblast, 184209
![](/img/style/loading.gif)