Formation of a submicrocrystalline structure in metastable austenitic steels during severe plastic deformation and subsequent heating
- Autores: Mal’tseva L.1, Mal’tseva T.1, Yurovskikh A.1, Raab G.2, Sharapova V.1, Vakhonina K.1
-
Afiliações:
- El’tsin Ural Federal University
- Ufa State Aviation Technical University
- Edição: Volume 2016, Nº 3 (2016)
- Páginas: 181-188
- Seção: Article
- URL: https://journals.rcsi.science/0036-0295/article/view/170371
- DOI: https://doi.org/10.1134/S0036029516030095
- ID: 170371
Citar
Resumo
The structure and the mechanical properties of metastable austenitic steels after severe plastic deformation by four or six passes of equal-channel angular pressing (ECAP) at a temperature of 400°C are studied. It is shown that ECAP results in strain hardening mainly due to the formation of a submicrocrystalline structure, which is retained after subsequent heating to 500°C.
Sobre autores
L. Mal’tseva
El’tsin Ural Federal University
Autor responsável pela correspondência
Email: mla44@mail.ru
Rússia, Yekaterinburg, 620083
T. Mal’tseva
El’tsin Ural Federal University
Email: mla44@mail.ru
Rússia, Yekaterinburg, 620083
A. Yurovskikh
El’tsin Ural Federal University
Email: mla44@mail.ru
Rússia, Yekaterinburg, 620083
G. Raab
Ufa State Aviation Technical University
Email: mla44@mail.ru
Rússia, Ufa, 450008
V. Sharapova
El’tsin Ural Federal University
Email: mla44@mail.ru
Rússia, Yekaterinburg, 620083
K. Vakhonina
El’tsin Ural Federal University
Email: mla44@mail.ru
Rússia, Yekaterinburg, 620083