Мақаланы E-mail арқылы жіберу Structure and Mechanical Properties of the Molybdenum–Steel Bimetal Fabricated by Hot Isostatic Pressing
- Авторлар: Makhina D.1,2, Denisov V.1, Perminova Y.1, Butrim V.1, Nikulin S.2
-
Мекемелер:
- JSC Kompozit
- National University of Science and Technology MISiS
- Шығарылым: Том 2019, № 10 (2019)
- Беттер: 1031-1035
- Бөлім: Advanced Materials and Technologies
- URL: https://journals.rcsi.science/0036-0295/article/view/173585
- DOI: https://doi.org/10.1134/S0036029519100173
- ID: 173585
Дәйексөз келтіру
Ашық рұқсат
Рұқсат берілді
Тек жазылушылар үшін
Аннотация
Abstract—The structure and the ultimate tensile strength of the bimetallic joints of a TsM2A (Mo–Ti–Zr system) molybdenum alloy and a corrosion-resistant 12Kh18N10T steel are studied. These joints are formed by diffusion welding under hot isostatic pressing conditions using the following combined intermediate layers: vanadium–electrical sheet steel, vanadium–copper, and titanium–niobium–copper. The highest strength of the joint (419 MPa) is reached when a combination intermediate layer of titanium, niobium, and copper is used.
Авторлар туралы
D. Makhina
JSC Kompozit; National University of Science and Technology MISiS
Хат алмасуға жауапты Автор.
Email: loskutovadn@gmail.com
Ресей, Korolev, 141070; Moscow, 119049
V. Denisov
JSC Kompozit
Email: loskutovadn@gmail.com
Ресей, Korolev, 141070
Yu. Perminova
JSC Kompozit
Email: loskutovadn@gmail.com
Ресей, Korolev, 141070
V. Butrim
JSC Kompozit
Email: loskutovadn@gmail.com
Ресей, Korolev, 141070
S. Nikulin
National University of Science and Technology MISiS
Email: loskutovadn@gmail.com
Ресей, Moscow, 119049