Magnetic Characteristics of Sintered (Pr,Dy)–(Fe,Co,Cu)–B Materials with Various Copper Contents as Functions of the Annealing Temperature


Дәйексөз келтіру

Толық мәтін

Ашық рұқсат Ашық рұқсат
Рұқсат жабық Рұқсат берілді
Рұқсат жабық Тек жазылушылар үшін

Аннотация

The effect of copper alloying on the coercive force and the residual induction of sintered materials (Pr0.53Dy0.47)13(Fe0.64Co0.36)resCuxB6 (x = 0–3 at %) annealed at various temperatures is considered. The dependences of coercive force HcI and residual induction Br on the copper content are found to be nonmonotonic. This fact is explained by that alloying with copper leads to a change in the phase composition, which is accompanied by an increase in the coercive force and the residual magnetization of the alloy, while a change in the chemical composition and the thickness of intergranular interlayers upon copper alloying leads to a decrease in the values of HcI and Br as the copper content increases.

Негізгі сөздер

Авторлар туралы

R. Valeev

All-Russia Institute of Aviation Materials

Email: rezchikovaii@mail.ru
Ресей, Moscow, 105005

I. Rezchikova

All-Russia Institute of Aviation Materials

Хат алмасуға жауапты Автор.
Email: rezchikovaii@mail.ru
Ресей, Moscow, 105005

E. Davydova

All-Russia Institute of Aviation Materials

Email: rezchikovaii@mail.ru
Ресей, Moscow, 105005

R. Morgunov

Institute of Problems of Chemical Physics, Russian Academy of Sciences

Email: rezchikovaii@mail.ru
Ресей, Chernogolovka, Moscow oblast, 142432

V. Piskorskii

All-Russia Institute of Aviation Materials

Email: rezchikovaii@mail.ru
Ресей, Moscow, 105005


© Pleiades Publishing, Ltd., 2019

Осы сайт cookie-файлдарды пайдаланады

Біздің сайтты пайдалануды жалғастыра отырып, сіз сайттың дұрыс жұмыс істеуін қамтамасыз ететін cookie файлдарын өңдеуге келісім бересіз.< / br>< / br>cookie файлдары туралы< / a>