Comparative analysis of the reactivity of nickel and a Ni–Re (10 wt %) alloy during direct current polarization in sulfuric acid solutions
- Авторлар: Bryukvin V.1, Skryleva E.2, Levchuk O.1, Tsybin O.1, Bol’shikh A.1, Kuznetsova O.1
-
Мекемелер:
- Baikov Institute of Metallurgy and Materials Science
- National Research Technological University MISiS
- Шығарылым: Том 2016, № 11 (2016)
- Беттер: 1049-1054
- Бөлім: Article
- URL: https://journals.rcsi.science/0036-0295/article/view/170990
- DOI: https://doi.org/10.1134/S0036029516110057
- ID: 170990
Дәйексөз келтіру
Аннотация
A comparative analysis of the reactivity of nickel and its alloy with rhenium during their direct current polarization in sulfuric acid solutions (50–150 g/L, 25–60°C) is carried out. The regions of anodic potentials of their active dissolution and passivation are determined on the basis of the analysis results. The chemical compositions of the passivation films of electrode polarization are determined by X-ray photoelectron spectroscopy. The mechanism of film formation is established. The influence of the depolarizing ability of rhenium in the alloy composition on the depassivation of the alloy is revealed and evaluated.
Авторлар туралы
V. Bryukvin
Baikov Institute of Metallurgy and Materials Science
Хат алмасуға жауапты Автор.
Email: brukvin@imet.ac.ru
Ресей, Leninskii pr. 49, Moscow, 119991
E. Skryleva
National Research Technological University MISiS
Email: brukvin@imet.ac.ru
Ресей, Leninskii pr. 4, Moscow, 119991
O. Levchuk
Baikov Institute of Metallurgy and Materials Science
Email: brukvin@imet.ac.ru
Ресей, Leninskii pr. 49, Moscow, 119991
O. Tsybin
Baikov Institute of Metallurgy and Materials Science
Email: brukvin@imet.ac.ru
Ресей, Leninskii pr. 49, Moscow, 119991
A. Bol’shikh
Baikov Institute of Metallurgy and Materials Science
Email: brukvin@imet.ac.ru
Ресей, Leninskii pr. 49, Moscow, 119991
O. Kuznetsova
Baikov Institute of Metallurgy and Materials Science
Email: brukvin@imet.ac.ru
Ресей, Leninskii pr. 49, Moscow, 119991
![](/img/style/loading.gif)