Coordination mechanism, characterization, and photoluminescence properties of spinel ZnAl2O4 nanoparticles prepared by a modified polyacrylamide gel route

详细

Single-phase ZnAl₂O₄ nanoparticles with the spinel structure were successfully synthesized using a modified polyacrylamide gel method according to the atomic ratio of Zn to Al = 1: 1.8. The as-prepared samples were characterized by means of X-ray powder diffraction (XRD), thermogravimetric analysis (TG), differential scanning calorimetry analysis (DSC), field-emission scanning electron microscopy (SEM), Fourier transform infrared spectroscopy (FTIR), and photoluminescence (PL) spectra. XRD patterns show that the pure phase of ZnAl₂O₄ is obtained after heating the xerogel at 900°C for 5 h in air. The SEM images reveal that the ZnAl₂O₄ nanoparticles have a narrow particle size distribution and the average particle size is around 45 nm. Photoluminescence (PL) spectra demonstrate the single phase ZnAl₂O₄ nanoparticles have an emission peak located at 469 nm when excited by 350 nm light. The phase structure, coordination mechanism, and luminescence properties have been discussed on the basis of the experimental results.