Electrospinning Fabrication of SrTiO3 Nanofibers and Their Photocatalytic Activity
- Авторы: Xu L.1,2,3, Zhao Y.2, Wang W.1, Liu H.1, Wang R.1
-
Учреждения:
- School of Textiles
- School of Material Science
- Research Center of Jifa Group Ltd.
- Выпуск: Том 92, № 6 (2018)
- Страницы: 1237-1241
- Раздел: Photochemistry and Magnetochemistry
- URL: https://journals.rcsi.science/0036-0244/article/view/170041
- DOI: https://doi.org/10.1134/S0036024418060092
- ID: 170041
Цитировать
Аннотация
SrTiO3 nanofibers were fabricated by an electrospinning process. The phase, microstructure and photocatalytic activity of the obtained SrTiO3 nanofibers were investigated. The XRD patterns and the SEM images suggest that SrTiO3 nanofibers with perovskite phase and rough surface have been fabricated in the current work. The SrTiO3 nanofibers show a high efficiency decomposition of RhB under ultraviolet light irradiation. The high photocatalytic activity of SrTiO3 nanofibers results from the large specific surface area. The large specific surface area provides more surface active sits and makes an easier charge carrier transport. On the basis of the photocatalytic performance of SrTiO3 nanofibers, the possible photocatalysis mechanism was proposed.
Ключевые слова
Об авторах
Lei Xu
School of Textiles; School of Material Science; Research Center of Jifa Group Ltd.
Автор, ответственный за переписку.
Email: leixu112@126.com
Китай, Tianjin, 300387; Tianjin, 300387; Qingdao, 266299
Yiping Zhao
School of Material Science
Email: leixu112@126.com
Китай, Tianjin, 300387
Wei Wang
School of Textiles
Email: leixu112@126.com
Китай, Tianjin, 300387
Hao Liu
School of Textiles
Email: leixu112@126.com
Китай, Tianjin, 300387
Rui Wang
School of Textiles
Email: leixu112@126.com
Китай, Tianjin, 300387