Preparation and electromagnetic wave absorption of RGO/Cu nanocomposite
- Авторлар: Zhang H.1, Tian X.2, Zhang X.2, Li S.3, Shen Y.3, Xie A.3
-
Мекемелер:
- School of Physics and Materials Science
- Key Laboratory of Materials Physics, Institute of Solid State Physics
- School of Chemistry and Chemical Engineering
- Шығарылым: Том 91, № 9 (2017)
- Беттер: 1771-1774
- Бөлім: Physical Chemistry of Nanoclusters and Nanomaterials
- URL: https://journals.rcsi.science/0036-0244/article/view/169702
- DOI: https://doi.org/10.1134/S0036024417090126
- ID: 169702
Дәйексөз келтіру
Аннотация
We use a facile pyrolysis method to prepare reduced graphene oxide and copper nanocomposite (RGO/Cu) based on it. The product shows an outstanding wave absorption properties. The maximum reflection loss is up to–50.7 dB at 3.8 GHz. The reflection loss of–10 dB (90% power absorption) corresponds to a bandwidth of 11.2 GHz (3.4–14.6 GHz range) for the layer thickness of 2–5 mm. Therefore, it is suggested that the RGO/Cu nanocomposite is also a new kind of lightweight and high-performance EM wave absorbing material.
Негізгі сөздер
Авторлар туралы
Hui Zhang
School of Physics and Materials Science
Хат алмасуға жауапты Автор.
Email: zhhui@ahu.edu.cn
ҚХР, Hefei, 230601
Xingyou Tian
Key Laboratory of Materials Physics, Institute of Solid State Physics
Email: zhhui@ahu.edu.cn
ҚХР, Hefei, 230031
Xian Zhang
Key Laboratory of Materials Physics, Institute of Solid State Physics
Email: zhhui@ahu.edu.cn
ҚХР, Hefei, 230031
Shikuo Li
School of Chemistry and Chemical Engineering
Email: zhhui@ahu.edu.cn
ҚХР, Hefei, 230601
Yuhua Shen
School of Chemistry and Chemical Engineering
Email: zhhui@ahu.edu.cn
ҚХР, Hefei, 230601
Anjian Xie
School of Chemistry and Chemical Engineering
Email: zhhui@ahu.edu.cn
ҚХР, Hefei, 230601