High-power (Nd, Dy)–(Fe, Co)–B magnets with a low temperature coefficient of induction

Аннотация

High-power (Nd, Dy)–(Fe, Co)–B permanent magnets with a low temperature coefficient of induction (α) were prepared using advantages of strip casting and low-oxygen technologies. The microstructure and temperature dependences of magnetic properties have been studied on sintered (Nd_{1 – x}Dy_x)_13.9(Fe_{1 – y}Co_y)_79.8Cu_0.1Ga_0.1B_6.1 magnets with 0.20 ≤ x ≤ 0.25 and 0 ≤ y ≤ 0.20. The increase in y from 0 to 0.20 is accompanied by an increase in the Curie temperature from 327 to 492°C. This favors a decrease in the value of α from 0.099 to 0.060%/°C, respectively. Magnets with an oxygen content of no more than 2500 ppm which were prepared from the (Nd_0.75Dy_0.25)_13.9(Fe_0.85Co_0.15)_79.8Cu_0.1 Ga_0.1B_6.1 alloy, have the following hysteresis characteristics at 140°C: B_r ≥ 11.3 kG, H_c ≥ 8 kOe, and (BH)_max ≥ 30 MGOe; in this case, α ≤ |–0.07%/°С|.