Monolithic FeOx/Al2O3 catalysts for ammonia oxidation and nitrous oxide decomposition

Аннотация

(1.2–8.3)%FeO_х/Al₂O₃ monolith catalysts have been prepared by impregnating alumina with aqueous solutions of iron(III) nitrate and oxalate and have been tested in NH₃ oxidation and in the selective decomposition of N₂O in mixtures resulting from ammonia oxidation over a Pt–Rh gauze pack under conditions of nitric acid synthesis (800–900°C). In the case of the support calcined at 1200°C, the catalyst is dominated by bulk Fe₂O₃ particles localized on the Al₂O₃ surface. The activity of these samples in both reactions decreases with a decreasing active component content, thus limiting the potential of Fe₂(C₂O₄)₃ · 5H₂O, an environmentally friendlier but poorly soluble compound, as a substitute for Fe(NO₃)₃ · 9H₂O. Decreasing the support calcination temperature to 1000°C or below leads to the formation of a highly defective Fe–Al–O solid solution in the (1.2–2.7)%FeO_х/Al₂O₃ catalysts. The surface layers of the solid solution are enriched with iron ions or stabilize ultrafine FeO_х particles. The catalytic activity of these samples in both reactions is close to the activities measured for ~8%FeO_х/Al₂O₃ samples prepared using iron nitrate.