An XPS Study of the Interaction of a Palladium Foil with NO2

Resumo

The interaction of a palladium foil with nitrogen dioxide in a temperature range of 30–450°C at three NO₂ pressures of 10^–6, 10^–5, and 10^–4 mbar was studied by X-ray photoelectron spectroscopy (XPS). In all cases, a three-dimensional oxide film was formed on the surface of palladium metal starting with a temperature of 150°C. Based on the measurements of the Pd 3d_5/2, Pd 3p_3/2, and O 1s binding energies and the [Pd] : [O] atomic ratio, it was found that the film consisted of the palladium oxide PdO. The oxide film thickness d was estimated based on the weakening of the Pd 3d line of metallic palladium. As the interaction temperature was increased, d initially increased to reach a maximum of ~3.5–5 nm; thereafter, it began to decrease due to the decomposition of PdO to a metallic state.