Low-Temperature Oxidation of Carbon Monoxide: The Synthesis and Properties of a Catalyst Based on Titanium Dioxide, Nanodiamond, and Palladium for CO Oxidation

Resumo

A catalyst based on TiO₂ and nanodiamond with a 10 wt % palladium content of the catalyst was synthesized. The effect of the nanodiamond content on the catalytic properties in a reaction of CO oxidation at room temperature and low concentrations of CO (<100 mg/m³) was studied. It was established that, at a nanodiamond content of the catalyst from 7 to 9 wt % and a palladium content of 10 wt %, the rate of CO oxidation reached a maximum, and it was higher by a factor of 2.5 than the rate of CO oxidation on a catalyst based on pure TiO₂, which included palladium clusters. With the use of transmission electron microscopy, XRD X-ray diffractometry, and X-ray photoelectron spectroscopy, it was found that the clusters of palladium covered with palladium oxide with an average cluster size of 4 nm were formed on the surface of the TiO₂ carrier. It was assumed that the catalyst synthesized is promising for applications in catalytic and photocatalytic air-cleaning systems.