- Autores: Startsev O.V.1, Lebedev M.P.2, Slavin A.V.1, Noev I.I.3
-
Afiliações:
- All-Russian Research Institute of Aviation Materials, State Scientific Center of the Russian Federation
- Larionov Institute of Physicotechnical Problems of the North, Siberian Branch, Russian Academy of Sciences
- Ammosov North-Eastern Federal University
- Edição: Volume 483, Nº 1 (2018)
- Páginas: 145-150
- Seção: Physical Chemistry
- URL: https://journals.rcsi.science/0012-5016/article/view/153800
- DOI: https://doi.org/10.1134/S0012501618120023
- ID: 153800
Citar
Resumo
The strength, impact toughness, and fractography of degradation of epoxy polymer and poly(methyl methacrylate) were studied during aging under conditions of moderate warm and warm humid climates. Heterogeneity of aging of the materials in thickness of specimens was detected. A common regularity of aging of amorphous and partially crystalline polymers is the formation of a degraded surface layer 100–200 μm thick. Principles of linear fracture mechanics were used to take into account the effect of this layer on the change in mechanical properties of polymers.
Sobre autores
O. Startsev
All-Russian Research Institute of Aviation Materials,State Scientific Center of the Russian Federation
Autor responsável pela correspondência
Email: startsev@gmail.com
Rússia, Moscow, 105005
M. Lebedev
Larionov Institute of Physicotechnical Problems of the North, Siberian Branch, Russian Academy of Sciences
Email: startsev@gmail.com
Rússia, Yakutsk, 677891
A. Slavin
All-Russian Research Institute of Aviation Materials,State Scientific Center of the Russian Federation
Email: startsev@gmail.com
Rússia, Moscow, 105005
I. Noev
Ammosov North-Eastern Federal University
Email: startsev@gmail.com
Rússia, Yakutsk, 677000
Arquivos suplementares